reinforced with GF PA66 modified nylon66 engineering plastic granules

Wear- resistant
30% GF
reinforced
Performance
Test condition
Testing standard
Units
AZ601
Mechanical property
Tensile modulus
50mm/min
ISO527-1/2
Mpa

Yield stress
50mm/min
ISO527-1/2
Mpa

Tensile strength
50mm/min
ISO527-1/2
Mpa
175
Elongation at break
5mm/min
50mm/min
ISO527-1/2
%
2.12
Bending modulus
2mm/min
ISO178
Mpa
9600
Bending strength
2mm/min
ISO178
Mpa
248
Charpy notched impact strength
23°C
ISO179/leA
KJ/m2
12.6
Charpy unnotched impact strength
23°C
ISO179/leA
KJ/m2
65
Thermal
Melting
DSC.10K/min
ISO3146
°C
265
Heat distortion temp. A
1.8Mpa
ISO75
°C
250
Heat distortion temp. B
0.45Mpa
ISO75
°C
255
Electrical property
Surface resistivity

IEC60093
Ohm
1/0.1
Volume resistivity

IEC60093
Ohm×cm
10/0.1
Anti-arc-track of
TestotutionA
IEC60012
V

Physical property
Density
23°C
ISO1183
g/cm3

Hygroscopicity
23°C,50%r.h
ISO62
%

Absorbent/water absorption
23°C
/saturtion
ISO62
%
0.9
Radial shrinkage
flow
ISO294-4
%
0.58
Transverse shrinkage
transverse
ISO294-4
%
0.25
Flame retardant
Flammability test
1.6/3.0mm
UL94


The level of flame-retardant test
1mm thickness
ISO3795
mm/min

Material description



PA66+30GF wear-resisitant MOS2