2011 sell well PVC Resin(Emulsion Grade)

PVC paste Resin consists of vinyl chloride monomer polymerization, can be made into all kinds of leather products.
PVC Resin (PB1302,PB-1152C,PB1202,PB1702) can be used in clothes leather, imitation leather, car letter, floor leather, wall paper, tent fabric and medical gloves, toy manufacture and wire coating layer.

Test items
unit



Specication




PB1152

PB1202
PB1302
PB1702
PB1311








Viscosity
ml/g
100-120

100-120
115-135
153-173
115-135
K value

68

68
70
79
70
degree of polymerization

900-1500

900-1150
1100-1350
1700-1950
1100-1350
surface density
g/cm3
0.30-0.45

0.30-0.45
0.30-0.45
0.30-0.45
0.30-0.45
heat loss
%<
0.4

0.4
0.4
0.4
0.4
average grain diameter
um
15+/-5

15+/-5
15+/-5
15+/-5
15+/-5
>90um

0

0
0
0
0
>50um

1

1
1
1
1
VCM vestigital
mg/kg<
5

5
5
5
5
plastipaste PVC ,DOP

100:100

100:60
100:60
100:60
100:100
Brinell viscosity
2hrs
6

3.0-7.0
3.0-7.0
3.0-7.0
20-50

24hrs
10

3.0-10
3.0-10
3.0-10.0
60-100

g/s






PVC :DOP

100:50:00

100:50:00
100:50:00
100:50:00
100:100
0.4Mpa

>2.4

>3.2
>3.2
>3.2
>2
0.8Mpa

>5

>8
>8
>8
Paste PVC is a homopolymer of PVC which is made by emulsion polymerization, It has incombustible feature and can be used for coating cloth, rotary forming, macerating, spraying and foaming after mixed with plasticizer and other addition agent. It has a light white and micro powder.

3..Usage : This product is a high-quality raw material in producing foam floor, wall paper, leathererette, soft and hard foam plastic for sound insulation and heat insulation, toy, glove,paperboard coat, conveying belt, fitting of car, adhesive and seal gum for car coated glass and so on.
4.Package : 20 / 25 kg pp woven bag or paper bag with inner lined plastic film,13.0 MT / 20 FCL
5. Store and transport: prevent from rain, snow, humid, sunshine, throwing and other mechanical damage